Gravity casting process of aluminum alloy wheel hub

发布时间:2020-08-29 15:56:03点击:13256

  Compared with low pressure casting, gravity casting has the following advantages: lower investment cost of production equipment and mold; For products with complex product structure, it is easier to use gravity casting than low pressure casting in process control. Due to the problem of product order, considering the production cost, some products with small order quantity need gravity casting production. Today, I will introduce the gravity casting technology of aluminum alloy wheel hub.


  The specific steps of melting the raw materials of aluminum alloy wheel hub are as follows: put the aluminum alloy melt into the melting chamber in the furnace to form aluminum alloy liquid. When the temperature of aluminum liquid reaches 730 ℃ to 750 ℃, stir with slag spoon for 2-3 minutes.

  In addition, the specific steps of refining and degassing the molten aluminum alloy raw materials are as follows: blowing the refining agent into the smelting chamber with nitrogen to remove the gas and non-metallic inclusions in the aluminum alloy melt, adding al SR master alloy, mixed rare earth and aluminum zirconium master alloy in the smelting furnace, modifying and refining the aluminum alloy melt entering the quenching and tempering room, and refining the aluminum alloy melt into the quenching and tempering room Nitrogen was blown into the quenching and tempering room to treat the aluminum alloy, and the melt was degassed twice.

  The specific pouring steps are as follows: the molten liquid in the service room is poured into the mold through the iron spoon for casting. For the products with thin spokes and difficult to increase cooling air, the wall thickness of the side mold corresponding to the hot section thickness increases, which increases the heat absorption capacity of the mold, so that the position can accelerate solidification, and the feeding channel can play a greater role under the same conditions.